3D Printing Metal Powder Spherical 316L Stainless Steel Powder
Advantage of EB China Stainless Steel Powder
Even powder composition, less impurities High sphericity Low oxygen content Good flowability High loose density, high tap density 316l Stainless steel powder is widely used in powder silver sintering, pressing, metal injection molding, thermal spraying, metal shot blasting and other industries.
| NO.: | 304(L) | 316(L) | 174PH |
| Production Process | Atomized | Atomized | Atomized |
| Grade: | 304(L) | 316(L) | 17-4PH |
| Density | App.4.1-4.5 Tap.>4.9 G/cm3 | App.4.1-4.5 Tap.>4.8 G/cm3 | App.4.1-4.5 Tap.>4.8 G/cm3 |
| Hardness | 34.5HRC | 36HRC | 35HRC |
| Size | 150um | 150um | 150um |
|
| 75um | 75um | 75um |
|
| 45um | 45um | 45um |
|
| 15um | 15um | 15um |
| Content | Cr:18-20 Ni:8-12 C:0.08(0.03) Si:1max Mn:2max Fe:bal. | Cr:16-18 Ni:10-14 Mo:2-3 C:0.08(0.03) Si:1max Mn:2max Fe:bal. | Cr:15.5-17.5 Ni:3-5 Nb:0.15-0.45 Cu:3-5 C:0.07 Si:1max Mn:1max Fe:bal. |
| Applications | MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.6g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 | MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.8g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 | MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.8g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 |